Mullen burst tester TP-K11 is used to measure the bursting strength of paper submitted to increasing hydraulic pressure. Used in testing bursting strength of all types of papers in the 0 to 1600 kPa range depending on clamp pressure. It has mechanically & electrically integrated modern design, with compact structure & easy for maintenance. The advantage of user-friendly operations, stable performance makes this tester an essential instrument for papermaking, packing, inspection and research.
| Measurement range | 0 to 1600 kPa |
| Accuracy | ± 0.5 % F.S. |
| Compression speed | 95 ± 5 ml/min |
| Clamp pressure | ≥ 430 kPa |
| Diameter of upper clamp | 30.5 ± 0.05 mm |
| Diameter of lower clamp | 33.1 ± 0.05 mm |
| Pneumatic pressure | 0.3 to 0.5 MPa |
| Film resistance | For bulge height = 9 mm, The pressure = 25 to 35 kPa |
| Dimension | 480×420×600 mm |
| Net weight | 65 kg |
| Power supply | AC220 V ± 10 % , 50 Hz |
- Large colored LCD touch screen display
- Bursting strength range 0 to 1600 kPa
- Use of hydraulic oil as the driving force to break the specimen
- Equipped with high precision sensors
- Equipped micro-computer control system
- Attachment for micro-printer with high print speed and low failure rate
- Specimen is broken , stores the maximum amount automatically
Mullen burst tester is used to measure bursting strength of paperboard, paper across paper industry, packaging industry, printing industry.
Paper Testing Instruments
COBB sample cutter TP-C30
- Sample diameter
- 125 mm
- Sample error
- ± 0.2 mm
- Sample Thickness
- 0.1 to 1.0 mm
Paper and cardboard thickness meter TP-E21
- Measuring range
- 0 to 20 mm
- Accuracy
- 0.01 mm
- Gauge
- Analogue gauge display
Folding endurance tester TP-M10
- Measuring scope
- 0 to 99999 s
- Folding angle
- 135° ± 2°
- Tensile scope
- 4.9 to 14.7 N
Plastic Testing Instruments
Primary adhesive tester TPAT-A10
- Inclined adjustable angle
- 0 to 40°
- Panel width
- 120 mm
- Test area width
- 80 mm
Vicat softening temperature & HDT machine TVHT-A10
- Operating temperature
- Ambient temperature to 300°C
- Heating rate
- 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
- Maximum temp. error with heating speed
- ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Falling Weight Impact Tester TFWT-A10
- Temperature range
- 10 to 35°C
- Maximum falling height
- 2000 mm
- Resolution of displacement
- 1 mm
Melt flow Indexer TMFI-A11
- Measuring range
- 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
Rubber Testing Instruments
Rubber low temperature brittleness tester TRBT-A10
- Temperature range
- -60°C to 0°C
- Temperature accuracy
- ± 0.5°C
- Impact speed
- 2 m/s ± 0.2 m/s
Rubber Low Temperature Brittleness Tester TRBT-A11
- Temperature control range
- Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
- Temperature accuracy
- ± 0.3 ℃
- Impact speed
- 0℃ to -30℃ around 2.5 ℃/min '-30℃ to -40℃ around 2.5 ℃/min '-40℃ to -70℃ around 2.0 ℃/min
No rotor rheometer TNRR-A10
- Temperature tester
- Room temperature to 200°C
- Temperature display resolution
- 0.1°C
- Temperature control accuracy
- ≤ ± 0.3°C
Rubber-weiss plasticity testing machine TRWM-A10
- Temperature range
- RT 50° to 300°
- Temperature accuracy
- ± 1°
- Measuring range
- 0.01 to 25 mm
NDT Testing Instruments
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Digital low load Vickers Hardness tester TDVH-A10
- Test force
- 9.8 N, 49 N, 98 N, 196 N, 294 N, 490 N
- Hardness value symbol
- HV1, HV5, HV10, HV20, HV30, HV250
- Error range in display
- ± 3.0 %, ± 2.0 %
Rockwell hardness meter TRHM-A11
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 1 to 30 S
Portable Vibration Calibrator LPVC-A10
- Frequency (continually adjustable)
- 10 Hz to1280 Hz + 0.01 %
- Amplitude acceleration ( at 30m/s2 pk )
- 40 Hz to 320 Hz + 0.3 dB + 1 digit
- Amplitude velocity ( at 25mm / sec pk )
- 40 Hz to 320 Hz + 0.5dB +1 digit
Other Testing Instruments
Popular Categories
Navigation
Contact Us Map