Pulp beating (refining) freeness tester TP-C10 is used to measure the rate of dilution of pulp suspended water materials and to determine de-watering time. It is adopted with spring pre-tightening mechanism keeps the rubber sealing ring of the sealing hammer body in contact with the bottom of the water filtering tube. This increases the sealing performance of the sealing hammer body.
| Measurement range | 0 to 100° SR |
| Sealed testing speed | 100 ± 10 mm/s |
| Volume of distilled water | 1000 ± 5 ml |
| Draining time | 149 ± 1 s |
| Residual water volume | 7.85 to 8 ml |
| Hydraulic pressure | >0.3 MPa |
| Dimension | 450×250×1100 mm |
| Net Weight | 40 kg |
- Use of Schopper-Riegler test method for designing
- Adopted with spring pre-tightening mechanism
- Measurement range 0 to 100° SR
- Equipped with manual compression seal cone
- Simple user–friendly operations
Pulp beating freeness tester has applications in pulp & paper industry, packaging industry.
Paper Testing Instruments
Bekk Smoothness tester TP-L20
- Measuring scope
- ( 1 to 9999) s, divided in to (1 to 15) s, (15 to 300) s, (300 to 9999) s, the automatic (no. more than 200 s)
- Accuracy
- ±0.1 s within 300 s
- Vacuum system volume (ml)
- Bigger volume: 380 ± 1 Smaller volume: 38 ± 1
COBB sample cutter TP-C30
- Sample diameter
- 125 mm
- Sample error
- ± 0.2 mm
- Sample Thickness
- 0.1 to 1.0 mm
Mullen burst tester TP-K11
- Measurement range
- 0 to 1600 kPa
- Accuracy
- ± 0.5 % F.S.
- Compression speed
- 95 ± 5 ml/min
Plastic Testing Instruments
Lasting adhesive tester TLAT-A10
- Standard roller
- 2000 ± 50 g
- Testing stations
- 3
- Dimension (L*W*H) tester
- 320×210×550 mm (3 stations)
Melt flow Indexer TMFI-A10
- Measuring range
- 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
Lasting adhesive tester TLAT-A11
- Standard roller
- 2000 ± 50 g
- Testing stations
- 6
- Dimension (L*W*H) tester
- 650×210×550 mm (6 stations)
Primary adhesive tester TPAT-A10
- Inclined adjustable angle
- 0 to 40°
- Panel width
- 120 mm
- Test area width
- 80 mm
Rubber Testing Instruments
DIN abrasion tester TDAT-A10
- Test arm weight
- 2.5 N
- Additional Loads
- 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N,
- Idler
- 150 mm
Rubber Low Temperature Brittleness Tester TRBT-A11
- Temperature control range
- Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
- Temperature accuracy
- ± 0.3 ℃
- Impact speed
- 0℃ to -30℃ around 2.5 ℃/min '-30℃ to -40℃ around 2.5 ℃/min '-40℃ to -70℃ around 2.0 ℃/min
Rubber low temperature brittleness tester TRBT-A10
- Temperature range
- -60°C to 0°C
- Temperature accuracy
- ± 0.5°C
- Impact speed
- 2 m/s ± 0.2 m/s
Rubber-weiss plasticity testing machine TRWM-A10
- Temperature range
- RT 50° to 300°
- Temperature accuracy
- ± 1°
- Measuring range
- 0.01 to 25 mm
NDT Testing Instruments
Portable Vibration Calibrator LPVC-A10
- Frequency (continually adjustable)
- 10 Hz to1280 Hz + 0.01 %
- Amplitude acceleration ( at 30m/s2 pk )
- 40 Hz to 320 Hz + 0.3 dB + 1 digit
- Amplitude velocity ( at 25mm / sec pk )
- 40 Hz to 320 Hz + 0.5dB +1 digit
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Rockwell hardness meter (motorized type) TRHM-B10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Brinell hardness test
- 306, 613, 1839 N
Rockwell hardness meter TRHM-A10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 0 to 30 S
Other Testing Instruments