Heat sealer THS-A10 works on heat press seal method, before start of the test, user needs to preset the heat seal temperature, pressure and dwell time values so as to finish the entire sealing process automatically just after pressing the start button. Equipped with digital P.I.D. temperature control technology ensures the preset temperature to be reached rapidly without any fluctuation. The specimen is placed in between the upper & lower jaws with independent temperature control of upper & lower jaws.
| Seal temperature | Room temperature -250°C |
| Control accuracy | ± 0.2°C |
| Dwell time | 0.1 S to 999.9 S |
| Dwell pressure | 0.05 to 0.7 MPa |
| Heating mode | Single and double heating surface |
| Dimension (L*B*H) | 400×280×380 mm |
| Net weight | 30 kg |
| Power supply | AC 220V/ 50Hz |
- Specially designed heat sealing jaws
- Digital PID controlled system
- Manual or pedal switch
- Anti-scald design
- Large size touch screen for smooth operations
- Independent temperature control for upper & lower jaws
Heat sealer is used in plastic film material packaging, soft packaging laminated film & others to heat seal material using temperature, heat, pressure.
Plastic Testing Instruments
Melt flow Indexer TMFI-A10
- Measuring range
- 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
Vicat softening temperature & HDT machine TVHT-A10
- Operating temperature
- Ambient temperature to 300°C
- Heating rate
- 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
- Maximum temp. error with heating speed
- ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Charpy/ Izod Impact Tester TCI-A10
- Impact Speed & Energy (charpy)
- 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J
- Impact energy (Izod)
- 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
- Resolution of impact energy
- 0.001 J
Paper Testing Instruments
Paper and cardboard thickness meter TP-E21
- Measuring range
- 0 to 20 mm
- Accuracy
- 0.01 mm
- Gauge
- Analogue gauge display
Vertical tensile tester TP-B20
- Sample (size) length
- 0 to 200 mm adjustable
- Sample width
- 15 mm
- Measuring range
- 0 to 30 N (tissue paper), 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N
Folding endurance tester TP-M10
- Measuring scope
- 0 to 99999 s
- Folding angle
- 135° ± 2°
- Tensile scope
- 4.9 to 14.7 N
Rubber Testing Instruments
Rubber Low Temperature Brittleness Tester TRBT-A11
- Temperature control range
- Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
- Temperature accuracy
- ± 0.3 ℃
- Impact speed
- 0℃ to -30℃ around 2.5 ℃/min '-30℃ to -40℃ around 2.5 ℃/min '-40℃ to -70℃ around 2.0 ℃/min
Rubber-weiss plasticity testing machine TRWM-A10
- Temperature range
- RT 50° to 300°
- Temperature accuracy
- ± 1°
- Measuring range
- 0.01 to 25 mm
Mooney viscometer TMV-A10
- Control temperature range
- Normal temperature to 200°C
- Temperature display resolution
- 0.01°C
- Temperature control accuracy
- ± 0.3°
No rotor rheometer TNRR-A10
- Temperature tester
- Room temperature to 200°C
- Temperature display resolution
- 0.1°C
- Temperature control accuracy
- ≤ ± 0.3°C
NDT Testing Instruments
Rockwell hardness meter TRHM-A11
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 1 to 30 S
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Digital low load Vickers Hardness tester TDVH-A10
- Test force
- 9.8 N, 49 N, 98 N, 196 N, 294 N, 490 N
- Hardness value symbol
- HV1, HV5, HV10, HV20, HV30, HV250
- Error range in display
- ± 3.0 %, ± 2.0 %
Rockwell hardness meter (motorized type) TRHM-B10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Brinell hardness test
- 306, 613, 1839 N
Other Testing Instruments